CX-AED370 type pure white acrylic anodic electrophoretic coating
- Product Model：
- Texture
- surface
- 在线咨询
1.product introduction
CX-AED370 type pure white acrylic anodic electrophoretic coating is made from the latest introduction of advanced formula technology in Japan, carefully made from imported raw and auxiliary materials, and has international quality free lead electrophoretic coatings. It is a pearlescent electrophoretic coating developed for the field of aluminum and magnesium alloy coating in China.
The products of this model have the following features:
1. The appearance of the film is smooth and glossy, and the whiteness is uniform.
2, super uniform electrophoresis ability, easy to adjust the bath.
3. The stability of the bath is good, no coating is hung, no special technology is needed, the coating management is easy, and a suitable renewal cycle should be given.
4, the coating efficiency is high, economical, no waste water discharge, lead free, green environmental protection.
5, film thickness uniformity, high hardness, good abrasion resistance, corrosion resistance, superior performance, elegant and natural color.
2. product quality index
CX-AED369 coating quality index
Inspection list | Varnish (transparent) | Test conditions |
Appearance | Smooth and smooth | Visual measurement |
Glossiness (60%) | ≥ 60 | Gloss meter |
Lacquer film hardness (H) | 4-5 | GB/T6739 |
The adhesion of the paddle method (1mm delimi) | 100/100 | GB/T9286 |
Salt resistant foggy 24h, CASS (R) | ≥9.5 | GB/T10125 |
Salt tolerance | After the test, no bubbles and other obvious changes | GB/T5237.3 |
Alkali resistance for 24 hours (R) | ≥9.5 | GB/T5237.3 |
Washing resistance | After test, no bubbles, shedding or other obvious changes were observed on the surface of the composite membrane. | GB/T5237.3 |
boiling water resistance | After testing, no bubbles, cracks, wrinkles, shedding or discoloration occurred in the paint film. | GB/T5237.3 |
3.Packaging and Storage
1.Package: 25L or 200L plastic barrel;
2.Storage: During storage, the product shall be kept ventilated and dry without direct sunlight, keep it far from heat and fire source, prevent ice under low temperature in winter. The storage period is 6 months from the production date under 0 - 30℃